CREAMELT® PLA-HI

BIOBASED 3D PRINTING FILAMENT WITH HIGH IMPACT STRENGTH AND ACCURATE PRINITNG QUALITY

DESCRIPTION

CREAMELT® PLA-HI is a biobased 3D printing filament with high impact strength. It is made from natural resourced PLA (Polylactic Acid), which is additionally modified with impact modifier that makes it more impact resistant rather than most other PLA on the market.

PLA-HI is easy to print with and gives accurate measurements due to minimal shrinkage of the material when cooling down. It has interesting mechanical properties, good layer adhesion and works with most 3D printers on the market.

CREAMELT® PLA-HI gives you the ability to build high precission objects with smooth surfaces and excellent impact resistance.

PRINTING GUIDELINES

PRINTING TEMPERATURE = 200…220 °C
PLATFORM TEMPERATURE = 50…60 °C (Heated bed is not needed, but recommended)
PRINT SPEED = 40…150 mm/s

MECHANICAL PROPERTIES )*

TENSILE MODULUS = 2440 MPa
TENSILE STRENGTH = 40 MPa
TENSILE STRAIN AT BREAK = 8…13 %
IMPACT STRENGTH = 80 kJ/m^2 (ISO 179 / 1eU CHARPY unnotched)
SHORE HARDNESS = not measured

* as measured by printed tensile bars at 23°C

PHYSICAL & THERMAL PROPERTIES

DENSITY = 1240 kg/m^3
MELTING POINT = 145…160 °C
GLASS TRANSITION POINT = 55…60 °C

TECHNICAL DATA SHEET